T1 - Influence of bioactive particles and onium salt on the physicochemical properties of experimental infiltrants
AU - Mathias, Caroline
AU - Gomes, Rafael Soares
AU - Pfeifer, Carmem Silvia
AU - Pedreira, Priscila Regis
AU - Damasceno, Janaina Emanuela
AU - Marchi, Giselle Maria
N1 - Publisher Copyright:
© (2023), (SciELO-Scientific Electronic Library Online). All Rights Reserved.
PY - 2023
Y1 - 2023
N2 - This study evaluated physicochemical properties of experimental infiltrants after addition of hydroxyapatite nanoparticles (HAp) or 58S bioactive glass (BAG) and diphenyliodonium hexafluorophosphate (DPI). The resin matrix was composed of TEGDMA/Bis-EMA (3:1), 0.5 mol% CQ, and 1 mol% EDAB. The blends received or not 0.5 mol% DPI and 10% wt BAG or HAp. Icon was used as commercial control. The groups were characterized by XRD, FT-IR spectrometry, and SEM before and after simulated body fluid (SBF) immersion for up to 7 days. Polymerization kinetics (n =3 ), water sorption and solubility (n=10), and viscosity (n = 3) were surveyed. For polymerization kinetics, the samples were polymerized for 5 min and the data were obtained from 40 s and 5 min. Statistical analysis was made using ANOVA and Tukey’s test (a = 0.05). After 7 days of SBF immersion, XRD and FT-IR showed that the HAp crystalline phase was present only in the HAp groups. A lower degree of conversion (DC) and polymerization rate were observed for the Icon and BAG groups, whereas HAp showed higher values. For the BAG group, DPI increased polymerization rate and DC in 40 s. After 5 min, all groups presented DC above 80%. In groups with particles, the HAp groups exhibited higher viscosity, whereas DPI groups showed a decrease in viscosity. Icon had the highest water sorption. To conclude, BAG neither improved the physicochemical properties studied, nor did it show bioactive properties. The addition of DPI reduced viscosity caused by particle addition and also attenuated the DC decrease caused by BAG addition. The addition of bioactive particles to infiltrants should be seen with caution because they increase viscosity and may not bring major clinical improvements that justify their use. DPI might be indicated only if any component is added to the infiltrant to act as a compensation mechanism.
AB - This study evaluated physicochemical properties of experimental infiltrants after addition of hydroxyapatite nanoparticles (HAp) or 58S bioactive glass (BAG) and diphenyliodonium hexafluorophosphate (DPI). The resin matrix was composed of TEGDMA/Bis-EMA (3:1), 0.5 mol% CQ, and 1 mol% EDAB. The blends received or not 0.5 mol% DPI and 10% wt BAG or HAp. Icon was used as commercial control. The groups were characterized by XRD, FT-IR spectrometry, and SEM before and after simulated body fluid (SBF) immersion for up to 7 days. Polymerization kinetics (n =3 ), water sorption and solubility (n=10), and viscosity (n = 3) were surveyed. For polymerization kinetics, the samples were polymerized for 5 min and the data were obtained from 40 s and 5 min. Statistical analysis was made using ANOVA and Tukey’s test (a = 0.05). After 7 days of SBF immersion, XRD and FT-IR showed that the HAp crystalline phase was present only in the HAp groups. A lower degree of conversion (DC) and polymerization rate were observed for the Icon and BAG groups, whereas HAp showed higher values. For the BAG group, DPI increased polymerization rate and DC in 40 s. After 5 min, all groups presented DC above 80%. In groups with particles, the HAp groups exhibited higher viscosity, whereas DPI groups showed a decrease in viscosity. Icon had the highest water sorption. To conclude, BAG neither improved the physicochemical properties studied, nor did it show bioactive properties. The addition of DPI reduced viscosity caused by particle addition and also attenuated the DC decrease caused by BAG addition. The addition of bioactive particles to infiltrants should be seen with caution because they increase viscosity and may not bring major clinical improvements that justify their use. DPI might be indicated only if any component is added to the infiltrant to act as a compensation mechanism.
KW - Dental Materials
KW - Hydroxyapatites
KW - Resins
KW - Synthetic
UR - http://www.scopus.com/inward/record.url?scp=85169998896&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85169998896&partnerID=8YFLogxK
U2 - 10.1590/1807-3107BOR-2023.VOL37.0088
DO - 10.1590/1807-3107BOR-2023.VOL37.0088
M3 - Article
C2 - 37672421
AN - SCOPUS:85169998896
SN - 1806-8324
VL - 37
JO - Brazilian oral research
JF - Brazilian oral research
M1 - e088
ER -